UTR9000 TECHNICAL DATA SHEET
PRODUCT DESCRIPTION 产品介绍
C-UV 9400 is an ABS like SL resin which has accurate and durable features. It is designed for solid state
SLA platforms. C-UV 9400 can be applied in master patterns, concept models, general parts and functional
prototypes in the field of automotive, medical and consumer electronics parts duability
building with UTR9000is over 9000 是一种具备精确和耐久特性的类ABS的立体光造型
树脂。它被用于固态激光的光固化成型法。UTR9000可应用于于汽车，医疗，消费电子等工业领域的
母模，概念模型，一般部件，功能性部件的制作。用UTR9000树脂制造的部件的耐久性长达6.5个月
以上。
TYPICAL FEATURES典型特点
-Liquid resin`s medium viscosity, so easy recoating, easy clean parts and machines 中等粘度的液态树脂，
确保其更容易涂层以及清洗部件和机器
-Improved strength retained, improved dimensions retention of parts in humid condition 在潮湿环境中具有
更好的强度及尺寸保持特性
-need minimal part finishing只需要极小的部件修饰
-Long shelf life in machine更长的实际使用期限
TYPICAL BENEFITS典型优点
-Need less part finishing time,easier post-curing 更少的部件完成时间
-Buliding accurate and high tough parts with an improved dimensional stability 能够建造精确和高韧性的
部件并提高了部件的尺寸稳定性
-High quality controls for vacuum casting parts 对于真空铸造部件的高质量控制
-Low shrink and good resistance to yellowing 低收缩和优异的耐黄变性
-Magnificent white color 华丽的白色外观
-Outstanding machinable SLA material 卓越的可加工性
上海联泰三维科技有限公司
Physical Properties – Liquid Material 液态材料的物理性能
Appearance外观 White白色
Density 密度 1.13g/cm
3
@ 25 ℃
Viscosity 粘度 355 cps @ 28 ℃
Dp 固化深度 0.145 mm
Ec 临界曝光量 9.3 mJ/cm
2
Building layer thickness
0.1mm
建造层厚
Mechanical Properties of Post-Cured Material 固化后材料的机械性能
MEASUREMENT测试项目 TEST METHOD 测试方法 VALUE 数值
90-minute UV post-cure 90分钟紫外固化
Hardness 硬度, Shore D ASTM D 2240 83
Flexural modulus 弯曲模量, Mpa ASTM D 790 2,692-2,775
Flexural strength 弯曲强度, Mpa ASTM D 790 69- 74
Tensile modulus 拉伸模量, MPa ASTM D 638 2,189-2,395
Tensile strength 拉伸强度, MPa ASTM D 638 27-31
Elongation at break 断裂延长率 ASTM D 638 12 -20%
Impact strength,notched lzod, J/m ASTM D 256 58 - 70
缺口冲击强度
Heat deflection temperature, ℃ ASTM D 648 @66PSI 52
热变形温度
Glass transition,Tg
玻璃化转变温度，℃ DMA，E”peak 62
Coefficient of thermal expension,
热膨胀系数, /℃ TMA(T Density 密度, g/cm 3 1.16 注：使用温度和保存温度不宜过高，请在25摄氏度以下使用；推荐使用和保存温度为18-25摄氏度。
2024年3月31日发(作者：益文思)
上海联泰三维科技有限公司
UTR9000 TECHNICAL DATA SHEET
PRODUCT DESCRIPTION 产品介绍
C-UV 9400 is an ABS like SL resin which has accurate and durable features. It is designed for solid state
SLA platforms. C-UV 9400 can be applied in master patterns, concept models, general parts and functional
prototypes in the field of automotive, medical and consumer electronics parts duability
building with UTR9000is over 9000 是一种具备精确和耐久特性的类ABS的立体光造型
树脂。它被用于固态激光的光固化成型法。UTR9000可应用于于汽车，医疗，消费电子等工业领域的
母模，概念模型，一般部件，功能性部件的制作。用UTR9000树脂制造的部件的耐久性长达6.5个月
以上。
TYPICAL FEATURES典型特点
-Liquid resin`s medium viscosity, so easy recoating, easy clean parts and machines 中等粘度的液态树脂，
确保其更容易涂层以及清洗部件和机器
-Improved strength retained, improved dimensions retention of parts in humid condition 在潮湿环境中具有
更好的强度及尺寸保持特性
-need minimal part finishing只需要极小的部件修饰
-Long shelf life in machine更长的实际使用期限
TYPICAL BENEFITS典型优点
-Need less part finishing time,easier post-curing 更少的部件完成时间
-Buliding accurate and high tough parts with an improved dimensional stability 能够建造精确和高韧性的
部件并提高了部件的尺寸稳定性
-High quality controls for vacuum casting parts 对于真空铸造部件的高质量控制
-Low shrink and good resistance to yellowing 低收缩和优异的耐黄变性
-Magnificent white color 华丽的白色外观
-Outstanding machinable SLA material 卓越的可加工性
上海联泰三维科技有限公司
Physical Properties – Liquid Material 液态材料的物理性能
Appearance外观 White白色
Density 密度 1.13g/cm
3
@ 25 ℃
Viscosity 粘度 355 cps @ 28 ℃
Dp 固化深度 0.145 mm
Ec 临界曝光量 9.3 mJ/cm
2
Building layer thickness
0.1mm
建造层厚
Mechanical Properties of Post-Cured Material 固化后材料的机械性能
MEASUREMENT测试项目 TEST METHOD 测试方法 VALUE 数值
90-minute UV post-cure 90分钟紫外固化
Hardness 硬度, Shore D ASTM D 2240 83
Flexural modulus 弯曲模量, Mpa ASTM D 790 2,692-2,775
Flexural strength 弯曲强度, Mpa ASTM D 790 69- 74
Tensile modulus 拉伸模量, MPa ASTM D 638 2,189-2,395
Tensile strength 拉伸强度, MPa ASTM D 638 27-31
Elongation at break 断裂延长率 ASTM D 638 12 -20%
Impact strength,notched lzod, J/m ASTM D 256 58 - 70
缺口冲击强度
Heat deflection temperature, ℃ ASTM D 648 @66PSI 52
热变形温度
Glass transition,Tg
玻璃化转变温度，℃ DMA，E”peak 62
Coefficient of thermal expension,
热膨胀系数, /℃ TMA(T Density 密度, g/cm 3 1.16 注：使用温度和保存温度不宜过高，请在25摄氏度以下使用；推荐使用和保存温度为18-25摄氏度。